SLS 3D Printing Services

///SLS 3D Printing Services
SLS 3D Printing Services2017-10-13T17:06:59+00:00

Durable – Flexible – Heat Resistant

Selective laser sintering, or SLS, produces parts by using a laser to melt and fuse powdered polymers. SLS materials are durable, flexible and heat resistant, making SLS great for functional prototypes. Demanding applications such as snap fits and living hinges are easily achievable with SLS materials. Because SLS produces parts with a smooth surface finish, using no support structures, it is ideal for cosmetic prototypes with complex geometry.

Surface: Gritty Detail: ■■■■
Strength:■■■■■ Price: ■■■■■
Build SizeLayer HeightTolerance
26"x13"x20"0.004″ – 0.006″±0.015″
sls 3d printed parts collection

SLS Materials

Nylon 12 PA

General purpose material, suitable for a variety of applications.

Tensile Strength6,815 psi46 Mpa
Tensile Modulus246,500 psi1,700 Mpa
Tensile Elongation15%15%
Flexural Strength6,850 psi57 Mpa
Flexural Modulus188.549 psi1,300 Mpa
Notched Impact0.8 ft-lb/in43 J/m
HDT @ 66 psi350 °F177 °C
HDT @ 264 psi187 °F86 °C

Nylon 12 GF

Glass-filled nylon, highly durable and flexible.

Tensile Strength5,200 psi36 Mpa
Tensile Modulus420,000 psi2,896 Mpa
Tensile Elongation1%1%
Flexural Strength8,800 psi61 Mpa
Flexural Modulus325.000 psi2,241 Mpa
Notched Impact0.8 ft-lb/in40 J/m
HDT @ 66 psi354 °F179 °C
HDT @ 264 psi273 °F134 °C

Nylon 12 AF

Aluminum-filled nylown, better surface finish than other varieties.

Tensile Strength4,628 psi32 Mpa
Tensile Modulus373,800 psi2,577 Mpa
Tensile Elongation1%1%
Flexural Strength7,832 psi54 Mpa
Flexural Modulus289.250 psi1,994 Mpa
Notched Impact0.8 ft-lb/in40 J/m
HDT @ 66 psi351 °F177 °C
HDT @ 264 psi279 °F137 °C

Nylon 12 HST

Glass-filled nylon. Higher strength and temp than standard GF.

Tensile Strength7,050 psi48 Mpa
Tensile Modulus800,000 psi5,500 Mpa
Tensile Elongation5%5%
Flexural Strength12,000 psi85 Mpa
Flexural Modulus640,000 psi4,412 Mpa
Notched Impact0.7 ft-lb/in37.4 J/m
HDT @ 66 psi363 °F184 °C
HDT @ 264 psi355 °F179 °C

Flex TPE

Designed to simulate TPE for prototyping rubber parts.

Tensile Strength262 psi1.8 Mpa
Tensile Modulus800,000 psi5,500 Mpa
Tensile Elongation5%5%
Flexural Modulus860 psi5.9 Mpa
Tear Resistance86 lb/in15.1 kN/m
Shore Hardness40 Scale A40 Scale A
Melting Point378 °F192 °C

Let’s Prototype Something

Get an quote on your SLS prototypes today.

Get a Quote

SLS Applications

SLS Features

sls 3d printed case

Highly Durable

SLS produces stronger parts with better layer adhesion than almost any other plastic 3D printing technology.

sls 3d printed snap buckle

Highly Flexible

Flexible materials allow SLS to be used for demanding applications, such as snap fits and living hinges.

sls 3d printed oil cap

Heat Resistant

Selective laser sintering materials have high heat deflection temperatures, averaging 350°F @66 psi.